牌号简介 About |
---|
CP741是一种低熔体流动速率的异相共聚物。具有广泛的分子量分布和通用的添加剂包装。CP 741具有低气味/味道转移、高熔融强度、良好的加工性能和优异的冲击强度,即使在低温下也能。应用:高冲击强度热成型包装;吹塑包装和一般技术零件;片材挤压 CP 741 is a low melt flow rate heterophasic copolymer. It has broad molecular weight distribution and general purpose additive package. CP 741 presents low odor/taste transfer, high melt strength, good processability and excellent impact strength even at low temperatures. Applications: Thermoformed packages with high impact strength; Blown packages and technical parts in general; Sheet extrusion with high impact resistance; Corrugated pipe extrusion for water drainage of sinks or washbasins. Processing: Thermoforming Blow Molding Extrusion |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.895 | g/cm³ | ASTM D792 |
密度 Density |
0.895 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
0.80 | g/10min | ISO 1133 |
230℃,2.16kg 230℃,2.16kg |
0.80 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-20℃,注塑成型 -20 ℃, injection molding |
50 | J/m | ASTM D256 |
23℃,注塑成型 23 ℃, injection molding |
ASTM D256 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180 | ||
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 180 | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,注塑 1.8 MPa, unannealed, injection molded |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火,注塑成型 0.45 MPa, unannealed, injection molded |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 3 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,注塑成型 Yield, injection molding |
MPa | ISO 527-2 | |
屈服,注塑成型 Yield, injection molding |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
屈服,注塑成型 Yield, injection molding |
% | ISO 527-2 | |
屈服,注塑成型 Yield, injection molding |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
1% 正割,注塑成型 1% cut, injection molding |
MPa | ISO 178 | |
1% 正割,注塑成型 1% cut, injection molding |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level 2 |
ISO 2039-2 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 压 力1 (10N) |
【新闻资讯】查看全部
巴陵石化年产2万吨热塑橡胶安装初次开车成功
2017-09-05 8月31日,中国石化巴陵石化合成橡胶事业部建成投产国内首套年产2万吨热塑橡胶SEPS(氢化苯乙烯/异戊二烯共聚物)工业化装置,聚合加氢单元首次投料开车取得圆满成功。 这标志巴陵石化成为全球第三家采用具有自主知识产权核心技术工业化生产SEPS的企业,填补我国SEPS产品研发生产的空白,打破美国和日本企业长期垄断的局面,在热塑橡胶成套技术创新研发中具有里程碑意义。SEPS是有“绿色橡胶”美誉的热塑性弹性橡胶SIS加氢后的高端环保“升级版”产品,不但保留了SIS优异的应用性能,还 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |