牌号简介 About |
---|
PP+PPE+PS。紫外线稳定。提高了注塑应用中的耐化学性和表面美观性。NSF61/UL94清单待定。 PP+PPE+PS. UV-stabilized. Improved chemical resistance and surface aesthetics in injection molded applications. NSF61/UL94 listings pending. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
0.988 | g/cm³ | ASTM D792 |
-- -- |
0.990 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
260℃,5.0kg 260℃,5.0kg |
16 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
260℃,5 kg 260℃,5 kg |
18.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD 3 |
0.060 到 0.080 | % | |
MD:3.2 mm MD:3.2 mm |
% | ||
TD:3.2 mm TD:3.2 mm |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 4 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 5 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
断裂 fracture 5 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 5 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
断裂 fracture 5 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 6 |
MPa | ASTM D790 | |
-- -- 7 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 7 , 8 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 6 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 9 |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 9 |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
|||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 10 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 10 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
-30℃ -30℃ 10 |
ISO 180/1U | ||
23℃ 23℃ 10 |
ISO 180/1U | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ||
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 11 | |
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ||
TD:-40~40℃ TD:-40~40℃ |
1/℃ |
备注 |
---|
3. Tensile Bar |
4. 50 mm/min |
5. 类型 1, 50 mm/min |
6. 1.3 mm/min |
7. 2.0 mm/min |
8. at Yield |
9. 80*10*4 sp=62mm |
10. 80*10*4 mm |
11. 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
陶氏化学等三位美企CEO加入特朗普制造业参谋委员会
2017-08-16 周一,三位美国企业的首席执行长退出了特朗普(Donald Trump)政府的制造业顾问委员会,此举显然是抗议特朗普未能迅速谴责在弗吉尼亚州夏洛茨维尔举行示威活动并卷入暴乱的白人至上主义者。 制药企业默克公司(Merck & Co. Inc., MRK)周一早间在Twitter上发布了来自该公司董事长兼CEO Kenneth Frazier的声明,称美国领导人必须尊重美国的基本价值观,旗帜鲜明地反对仇恨、偏执和种族优越论,这种言论与人皆生而平等的美国理想背道而驰。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |