牌号简介 About |
---|
NORYL™ NHP6012树脂提供一流的非氯化/非溴化阻燃性,含有10%玻璃纤维;用途:电池模块电芯框架● 电池组顶盖● 电动汽车电池(EV)应用● 电池外壳● 电动车部件● 薄壁应用●薄壁产品。 |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PPE+PS Polyphenylene oxide + polystyrene blend
用途:薄壁应用;电池;
性能特点: 尺寸稳定性好; 电气性能; 吸水率低; 流动性高; 低密度; Low density,Low or no water absorption,Good Dimensional Stability,High liquidity
填料:玻璃纤维 10
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
比重 proportion |
|||
|
1.19 | g/cm³ | ISO 1183 |
|
1.19 | g/cm³ | ASTM D 792 |
收缩率 Shrinkage rate |
|||
流动 flow |
0.5~0.7 | % | |
垂直 vertical |
0.5~0.7 | % | |
吸水率 Water absorption rate |
|||
23°C饱和 23 ° C saturation |
0.2 | % | ISO 62 |
23°C 24hr 23°C 24hr |
% | ISO 62 | |
23°C 50RH平衡 23 ° C 50RH balance |
% | ISO 62 | |
23°C 50RH 24hr 23°C 50RH 24hr |
% | ISO 62 | |
23°C饱和 23 ° C saturation |
% | ASTM D570 | |
23°C 24hr 23°C 24hr |
% | ASTM D570 | |
熔融指数 Melt index |
|||
280℃10kg 280℃10kg |
cm³/10min | ISO 1133 | |
洛氏硬度 Rockwell hardness |
|||
M标尺 M scale |
ISO 2039 | ||
M标尺 M scale |
ASTM D785 | ||
球压硬度 Ball hardness |
|||
H358/30 H358/30 |
MPa | ISO 2039 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
1.0mm/min 1.0mm/min |
MPa | ISO 527 | |
5mm/min 5mm/min |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
断裂5mm/min Fracture 5mm/min |
MPa | ISO 527 | |
断裂5mm/min Fracture 5mm/min |
MPa | ASTM D638 | |
伸长率 elongation |
|||
断裂5mm/min Fracture 5mm/min |
% | ISO 527 | |
断裂5mm/min Fracture 5mm/min |
% | ASTM D638 | |
弯曲强度 bending strength |
|||
2.0mm/min 2.0mm/min |
MPa | ISO 178 | |
1.3mm/min 1.3mm/min |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
|||
2.0mm/min 2.0mm/min |
MPa | ISO 178 | |
1.3mm/min 1.3mm/min |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23°C 4.0mm 23°C 4.0mm |
KJ/m² | ISO 180 | |
-30°C 40mm -30°C 40mm |
KJ/m² | ISO 180 | |
23°C 23°C |
J/m | ASTM D256 | |
-30C -30C |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23°C 4.0mm 23°C 4.0mm |
KJ/m² | ISO 180 | |
-30°C 40mm -30°C 40mm |
KJ/m² | ISO 180 | |
23°C 23°C |
J/m | ASTM D4812 | |
-30C -30C |
J/m | ASTM D4812 | |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23°C 4.0mm 23°C 4.0mm |
kJ/m² | ISO 179 | |
23°C 4.0mm 23°C 4.0mm |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23°C 4.0mm 23°C 4.0mm |
kJ/m² | ISO 179 | |
-30°C 40mm -30°C 40mm |
kJ/m² | ISO 179 | |
仪表冲击 Instrument shock |
|||
23°C峰值能量 23 ° C peak energy |
J | ASTM D3763 | |
23°C总能量 23 ° C total energy |
J | ASTM D3763 | |
23°C峰值力 23 ° C peak force |
N | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1. 8MPa 4. 0mm 1. 8MPa 4. 0mm |
℃ | ISO 75 | |
0.45MPa 4 0mm 0.45MPa 4 0mm |
℃ | ISO 75 | |
未退火1. 8MPa 3.2mm Unannealed 1.8MPa 3.2mm |
℃ | ASTM D648 | |
未退火0.45MPa 3.2mm Unannealed 0.45MPa 3.2mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
|||
50°C/hr 10N 50°C/hr 10N |
℃ | ISO 306 | |
50°C/hr 50N 50°C/hr 50N |
℃ | ISO 306 | |
120°C/hr 50N 120°C/hr 50N |
℃ | ISO 306 | |
50°C/hr 10N 50°C/hr 10N |
℃ | ASTM D1525 | |
50°C/hr 50N 50°C/hr 50N |
℃ | ASTM D1525 | |
120°C/hr 50N 120°C/hr 50N |
℃ | ASTM D1525 | |
线膨胀系数 Linear expansion coefficient |
|||
流动 -40 0~40°C Flowing -40 ° C to 40 ° C |
cm/cm/°C | ISO 11359 | |
垂直 -40.0~40°C Vertical -40.0~40 ° C |
cm/cm/°C | ISO 11359 | |
流动 -40 0~40°C Flowing -40 ° C to 40 ° C |
cm/cm/°C | ASTM E831 | |
垂直 -40.0~40°C Vertical -40.0~40 ° C |
cm/cm/°C | ASTM E831 | |
导热系数 Thermal conductivity coefficient |
|||
|
W/m/K | ISO 8032 | |
|
W/m/K | ASTM D5930 | |
球压测试 Ball pressure test |
℃ | IEC 60695-10-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
|
ohms·cm | IEC 60093 | |
|
ohms·cm | ASTM D257 | |
表面电阻率 Surface resistivity |
|||
|
ohms | IEC 60093 | |
|
ohms | ASTM D257 | |
绝缘强度 Insulation strength |
|||
0.80mm在油中 0.80mm in oil |
kV/mm | IEC 60243 | |
3.2mm在油中 3.2mm in oil |
kV/mm | IEC 60243 | |
1.6mm在空气中 1.6mm in air |
kV/mm | IEC 60243 | |
3 .2mm在空气中 3.2mm in air |
kV/mm | IEC 60243 | |
介电常数 Dielectric constant |
|||
50/60Hz 50/60Hz |
IEC 60250 | ||
1MHz 1MHz |
IEC 60250 | ||
50/60Hz 50/60Hz |
ASTM D150 | ||
1MHz 1MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
50/60Hz 50/60Hz |
IEC 60250 | ||
1MHz 1MHz |
IEC 60250 | ||
50/60Hz 50/60Hz |
ASTM D150 | ||
1MHz 1MHz |
ASTM D150 | ||
CTI CTI |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.5mm 1.5mm |
UL 94 | ||
2.5mm 2.5mm |
UL 94 | ||
2.5mm 2.5mm |
UL 94 | ||
1.0mm 1.0mm |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
1.5mm 1.5mm |
℃ | IEC 60695 | |
3.0mm 3.0mm |
℃ | IEC 60695 | |
1.0mm 1.0mm |
℃ | IEC 60695 | |
2.0mm 2.0mm |
℃ | IEC 60695 | |
灼热丝相对温度 Relative temperature of heating wire |
|||
1.5mm 1.5mm |
℃ | IEC 60695 | |
3.0mm 3.0mm |
℃ | IEC 60695 | |
2.0mm 2.0mm |
℃ | IEC 60695 | |
1.0mm 1.0mm |
℃ | IEC 60695 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
华峰集团增资287亿元,布局千亿新材料产业园
2022-07-13 7月7日,千亿元重庆华峰新材料产业园战略合作签约仪式在重庆举行。下一步,华峰集团将投资287亿元在涪陵建设新材料集成项目,帮助将工业园区建设成为千亿级。 涪陵区和华峰集团 |
华峰集团增资287亿元,布局千亿新材料产业园
7月7日,千亿元重庆华峰新材料产业园战略合作签约仪式在重庆举行。下一步,华峰集团将投资287亿元在涪陵建设新材料集成项目,帮助将工业园区建设成为“千亿级”。
涪陵区和华峰集团在杭州签订华峰重庆低碳研究院合作协议
重庆华峰新材料产业园(以下简称“重庆华峰”)是中国500强企业、国内新材料产业龙头企业华峰集团2010年在重庆涪陵白岛新材料科技城投资建设的新材料产业基地。目前拥有华峰化工、华峰氨纶、华峰铝业、华峰新材料等9家独立法人公司,已建成己二酸100万吨/年、铝传热复合材料20万吨/年等项目,成为全球最大的己二酸和氨纶生产基地。预计今年重庆华丰工业总产值将突破350亿元。
近年来,该基地率先攻克己二腈“卡脖子”技术,填补国内空白,荣获中国石油化工联合会2021科技进步一等奖。
华峰集团在前期优质发展的基础上,继续深入培育重庆市场,布局千亿新材料产业园。目前,重庆华丰正在建设40万吨/年己二酸、30万吨/年差别化氨纶、20万吨/年己二腈/己二胺、25万吨/年尼龙66、15万吨/年高端汽车铝板箔等项目,总投资120亿元。建成后,重庆华丰年产值将达到800多亿元。
此外,公司将投资100亿元建设新材料整合项目,强化和拓展以页岩气为原料的产业链,项目投产后产值将超过200亿元。随着其他相关投资项目的到位,重庆华丰新材料产业园有望在几年内建成“千亿级”。
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- 电池模块及外壳
- 2021-12-03 0
- NORYL™ NHP6012和NHP6011 树脂提供一流的非氯化/非溴化阻燃性,分别含有10%,8%玻璃纤维;用途:电池模块电芯框架● 电池组顶盖● 电动汽车电池(EV)应用● 电池外壳● 电动车部件● 薄壁应用●薄壁产品。
- 阅读全文
电池模块及外壳
1-良好的阻燃性和冲击强度;
2-符合UL94 V-0标准;
3-尺寸稳定性和良好的流动性;
4-提供出色的介电性能,相对电痕指数 (CTI) 为 2,有助于避免紧密堆积的电池之间的电短路。
5-机械性能好;
6-NORYL NHP6011 和 NHP6012 树脂与聚碳酸酯(PC)相比具有优异的耐酸性,与聚酰胺相比具有更好的防潮性,并且具有较低的比重。
2-符合UL94 V-0标准;
3-尺寸稳定性和良好的流动性;
4-提供出色的介电性能,相对电痕指数 (CTI) 为 2,有助于避免紧密堆积的电池之间的电短路。
5-机械性能好;
6-NORYL NHP6011 和 NHP6012 树脂与聚碳酸酯(PC)相比具有优异的耐酸性,与聚酰胺相比具有更好的防潮性,并且具有较低的比重。
收起
- NORYL树脂光伏接线盒
- 2022-10-18 0
- NORYL树脂具有优秀的尺寸稳定性、电气和热性能,能耐受-40°C至140°C的温度,长期在户外的湿热环境使用后,还可保持85%以上的性能,且具有低翘曲特性,满足对接线盒材料的高要求
- 阅读全文
NORYL树脂光伏接线盒
1-NORYL树脂具有优秀的尺寸稳定性、电气和热性能,能耐受-40°C至140°C的温度;
2-长期在户外的湿热环境使用后,可保持85%以上的性能;
3-具有低翘曲特性,满足对接线盒材料的高要求,如设计的灵活性、无氯无溴阻燃、易安装性等;
4-可降低系统成本,符合严格的全球监管标准。
2-长期在户外的湿热环境使用后,可保持85%以上的性能;
3-具有低翘曲特性,满足对接线盒材料的高要求,如设计的灵活性、无氯无溴阻燃、易安装性等;
4-可降低系统成本,符合严格的全球监管标准。
收起
抱歉!暂无数据。