牌号简介 About |
---|
Eastman很高兴宣布推出Drystar*共聚酯。该新产品线是为满足变换器对共聚酯干燥要求寻求增值解决方案的需要而设计的。伊士曼?S共聚酯因其优异的美学、冲击强度和耐化学性等性能平衡而受到高度重视。当树脂按照推荐的干燥条件和设备适当脱水时,这些性能可以得到最佳的实现。认识到这一价值,Eastman构想了Drystar共聚酯,允许转换器有限地访问干燥剂烘干机,以实现这些优化。此外,一些带有干燥剂烘干机的转换器可能仍然发现Drystar共聚酯的价值增加,通过在注塑、型材挤压或挤出吹塑共聚酯之前去除干燥过程,从而获得生产灵活性和成本节约。最初的发布包括四个等级的Drystar共聚酯的商业化,Eastman正在进行计划,以在未来扩展这一战略产品线。*Drystar仅在亚太地区提供。 Eastman is pleased to announce the launch of DRYSTAR* copolyesters. This new product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman?s copolyesters are highly valued for their excellent balance of properties such as superior aesthetics, impact strength, and chemical resistance. These properties can be optimally realized when the resins are properly dehydrated in accordance to recommended drying conditions and equipment. Recognizing this value, Eastman conceived Drystar™ copolyesters to allow converters with limited access to desiccant dryers to achieve these optimizations. In addition, some converters with desiccant dryers may still find Drystar™ copolyesters value-adding to attain production flexibility and cost saving by removing the drying process prior to injection molding, profile extruding, or extrusion blow molding copolyesters. The initial launch comprises of the commercialization of four grades of Drystar™ copolyesters and Eastman has on-going program to extend this strategic product-line in the future. *DRYSTAR is only available in the Asia Pacific Region. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
1.27 | g/cm³ | ASTM D792 , ASTM D1505 |
23℃ 23℃ |
1.27 | g/cm³ | ISO 1183/D |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.13 | % | ASTM D570,ISO 62 |
固有粘度 Intrinsic viscosity 2 |
内部方法 | ||
薄膜,23℃ Thin film, 23 ℃ |
0.70 | 内部方法 | |
Pellets:23℃ Pellets:23℃ |
0.75 | 内部方法 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
µm | ||
割线模量 Secant modulus |
ASTM D882 | ||
MD MD |
MPa | ASTM D882 | |
TD TD |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
MPa | ASTM D882 | |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
MD,断裂 MD, fracture |
MPa | ASTM D882 | |
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,屈服 MD, yield |
% | ASTM D882 | |
TD,屈服 TD, yield |
% | ASTM D882 | |
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 3 |
ASTM D1709A | ||
-18℃ -18℃ |
g | ASTM D1709-A | |
23℃ 23℃ |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD MD |
g | ASTM D1922 | |
TD TD |
g | ASTM D1922 | |
裤型撕裂耐性 Pant tear resistance 4 |
ISO 6383-1 | ||
MD MD |
N/mm | ISO 6383-1 | |
TD TD |
N/mm | ISO 6383-1 | |
透氧率 Oxygen permeability |
|||
23℃ 23℃ |
cm³·mm/m²/atm/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance |
|||
38℃,100% RH 38℃,100% RH |
g/m²/24 hr | ASTM F1249 | |
二氧化碳渗透性 Carbon dioxide permeability 5 |
|||
23℃ 23℃ 5 |
cm³·mm/m²/atm/24 hr | ASTM D1434 | |
抗撕裂蔓延性 Tear resistant vine ductility 6 |
ASTM D1938 | ||
M.D.:23℃ M.D.:23℃ |
kN/m | ASTM D1938 | |
T.D.:23℃ T.D.:23℃ |
kN/m | ASTM D1938 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-40℃ -40℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-40℃ -40℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-40℃,3.2 mm -40℃,3.2 mm |
ASTM D4812 | ||
-30℃,3.2 mm -30℃,3.2 mm |
ASTM D4812 | ||
-20℃,3.2 mm -20℃,3.2 mm |
ASTM D4812 | ||
23℃,3.2 mm 23℃,3.2 mm |
ASTM D4812 | ||
-40℃ -40℃ 7 |
ISO 180/1U | ||
-30℃ -30℃ 7 |
ISO 180/1U | ||
-20℃ -20℃ 7 |
ISO 180/1U | ||
23℃ 23℃ 7 |
ISO 180/1U | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
-40℃,2.50 mm,Energy at Peak Load -40℃,2.50 mm,Energy at Peak Load |
J | ASTM D3763 | |
-40℃,3.20 mm,Energy at Peak Load -40℃,3.20 mm,Energy at Peak Load |
J | ASTM D3763 | |
23℃,2.50 mm,Energy at Peak Load 23℃,2.50 mm,Energy at Peak Load |
J | ASTM D3763 | |
23℃,3.20 mm,Energy at Peak Load 23℃,3.20 mm,Energy at Peak Load |
J | ASTM D3763 | |
-40℃,2.50 mm,能量到力量峰值 -40 ℃, 2.50 mm, energy to peak force 8 , 9 |
J | ISO 6603-2 | |
-40℃,3.20 mm,能量到力量峰值 -40 ℃, 3.20 mm, energy to peak force 8 , 9 |
J | ISO 6603-2 | |
23℃,2.50 mm,能量到力量峰值 23 ℃, 2.50 mm, energy to peak force 8 , 9 |
J | ISO 6603-2 | |
23℃,3.20 mm,能量到力量峰值 23 ℃, 3.20 mm, energy to peak force 8 , 9 |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-30~40℃ MD:-30~40℃ |
1/℃ | ASTM D696 | |
比热 specific heat |
DSC | ||
60℃ 60℃ |
J/kg/℃ | DSC | |
100℃ 100℃ |
J/kg/℃ | DSC | |
150℃ 150℃ |
J/kg/℃ | DSC | |
200℃ 200℃ |
J/kg/℃ | DSC | |
250℃ 250℃ |
J/kg/℃ | DSC | |
导热系数 Thermal conductivity coefficient |
|||
23℃ 23℃ |
W/m/K | ASTM C177 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength 10 |
|||
23℃ 23℃ 10 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
23 ℃,1 kHz 23 ℃,1 kHz |
ASTM D150 | ||
23 ℃,1 MHz 23 ℃,1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
23℃,1 kHz 23℃,1 kHz |
ASTM D150 | ||
23℃,1 MHz 23℃,1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45° 45° |
ASTM D2457 | ||
透光率 Transmittance |
ASTM D1003 | ||
常规 routine |
% | ASTM D1003 | |
总计 total |
% | ASTM D1003 | |
透明度 transparency |
ASTM D1746 | ||
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
R 级 R-level |
ISO 2039-2 | ||
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ASTM D638 , ISO 527-2 | |
拉伸强度 tensile strength |
ASTM D638 , ISO 527-2 | ||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 , ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 , ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D790 | |
撕裂阻力 Tear resistance |
ASTM D2582 | ||
M.D.:23℃ M.D.:23℃ |
N | ASTM D2582 | |
T.D.:23℃ T.D.:23℃ |
N | ASTM D2582 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 EMN-A-AC-GV-1 |
3 12.7 mm dia. head, 127 mm dia. clamp, 600 mm drop |
4 7.9 in/min |
5 50% RH |
6 254 mm/min, Split Tear Method |
7 4 mm |
8 13.5 ft/sec, 0.79 in 冲击器直径 |
9 40 mm support and clamp diameter |
10 500 V/sec, 方法A(短时间) |
【新闻资讯】查看全部
精业机器探究二十载 培养中空成型技术新巅峰
2017-12-05 日常生活中,厚壁霜膏罐被广泛应用于化妆品包装行业,业内皆知,中高档化妆品对包装瓶的要求尤为严苛。而中空成型技术的精湛程度直接决定了小小包装瓶的品质优劣。 第19届 DMP东莞 |
精业机器探究二十载 培养中空成型技术新巅峰 生活起居中,厚壁管霜膏罐被广泛运用于化妆品包装领域,业界周知,中高端化妆品对包装瓶的规定尤其苛刻。而空心成形技术性的高超水平立即决策了小小的包装瓶的质量好坏。
第19届 DMP东莞市国际性模具及金属加工、橡塑料及包装展会当场 前不久,东莞隆重召开的“2017第19届 DMP东莞市国际性模具及金属加工、橡塑料及包装展会”当场,柳州市精业设备有限责任公司(通称:精业设备)展览的“自动式注-吹中空成型机”相互配合“一出二腔”的PETG模具,吸引住了化妆品包装商的诸多眼光。据统计,该机器设备更是生产制造高中档化妆品包装――厚壁管霜膏罐的专用设备。
高超的手艺 晶莹层次感的来源于 在空心成型业内,精业设备早已因其“竖直式注坯注吹成形加工工艺”、“往复式转动二工序注吹、注拉吹加工工艺成形方法”,及高超的空心成形技术性而被业界熟识。 本次展览会,精业设备展览的“自动式注―吹中空成型机”就凭着其高超的技术性加工工艺遭受当场观众们的一致五星好评。据精业设备详细介绍,该机器设备在生产制造厚壁管霜膏罐时,可依据产品型号尺寸、生产量规定等开展配对生产制造,可可用的原材料包含PETG,Tritan,PC,PMMA等;其产品壁厚达到7mm。 根据精业设备的发明专利,注坯与吹瓶呈180º对称性遍布,二种加工工艺另外开展,自动化技术水平高。精业设备根据对模具与生产工艺流程的严苛操控,使商品的外型晶莹透亮,展现出夹层玻璃一样的层次感,进而考虑了日化行业对包裝质量的高规定。
精业设备自动式“注-吹”中空成型机 技术人员 精业设备前行的先锋队 迄今,精业设备已获4项我国专利发明技术性,12项发明专利发明专利,及其多种已经申请办理中的技术性专利权。在其中,精业设备创新的“竖直式注坯注吹加工工艺”,“两工序往复转动技术性”和“复合型芯技术性”特别是在具有象征性。 而这一系列科技成果与精业设备的技术人员紧密联系。二十年技术性沉定与工作经验累积,使精业设备在国际性范畴内推动着注坯注吹加工工艺前行的脚步。据统计,在这里批技术专业技术人才中,不仅有享有我国政府特殊津贴的老权威专家,也是有技术专业学识渊博、社会经验丰富多彩的青年技术骨干,她们拥有近千百种空心器皿开发设计的工作经验和整体实力。 现阶段,精业设备的主营业务商品包含“注-吹”系列产品、“注-拉-吹”系列产品20好几个型号规格,适用HDPE,LDPE,PP,PS,PC,PETG,PET,TRITAN,PES,PPSU等原材料,产品范畴最少可生产制造2mL,较大 现阶段早已生产制造到15升。商品运用范畴普遍,现阶段已包含医药设备,化妆品包装,食品类饮料(如乳酸菌饮料,酸奶等),健身运动水瓶座,婴儿奶瓶等行业。
复合型空心楼盖技术性 使独特原材料生产制造变成很有可能 由精业设备独自一人开发设计的自主创新技术性――复合型空心楼盖技术性在中国技术领域亦首屈一指。在同一根空心楼盖上,运用该技术性就可以完成将空气压缩吹进型坯內部,另外又在空心楼盖內部循环系统新闻媒体物质(如油、水等新闻媒体物质)。这一与众不同的技术性,让生产制造独特的原材料变成很有可能,例如高全透明的PC和PETG等原材料。 生活起居中,大家比较普遍的婴儿奶瓶,(太空杯)运动水杯、高清晰度护肤品器皿等高端商品均是根据该项技术性生产制造而成,其商品外型精致、瓶体全透明清亮。 针对吹瓶领域来讲,生产加工生产制造高全透明的商品十分颇具趣味性。现阶段,精业设备每一年为顾客生产制造的该类商品做到近千种。 总结: 自一九九七年至今,精业设备以“探索者”的角度,在空心成形技术性发展趋势路面上,全身心刻苦钻研,以寻找更大提升。在每一个技术性转折点与升級的大关,必然经历过重重的千难万险,提升逐层技术要求,才得到获得如今的研究成果。二十年技术性承传,铸就中国注拉吹空心成形技术性新顶峰,在未来的发展史中,精业设备空心成形技术性又将展现出如何的新姿势,大家且翘首以待! 来源于:我国塑料机械网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |