牌号简介 About |
---|
Styrolux® 684D是一种透明的苯乙烯-丁二烯共聚物(SBC),用于增强韧性的零件的注射成型,以及片材和薄膜挤出和吹塑成型。Styrolux® 684D制成的零件显示出优异的印刷性能。特点:高清晰度、高韧性、良好的印刷性、高透气性、符合水蒸气法规的应用、食品包装容器、杯子和盖子、玩具、挤压片和薄膜医疗设备 Styrolux® 684D is a clear styrene-butadiene copolymer (SBC) used in injection molding for parts with enhanced toughness as well as in sheet and film extrusion and blow molding. Parts made of Styrolux® 684D reveal excellent printability. FEATURES High clarity Improved toughness Good printability High permeability to gases and water vapor Regulatory compliant APPLICATIONS Food packaging Container, cups and lids Toys Extruded sheet and thin film Medical devices |
产品描述 Product Description
厂家:瑞士英力士苯领 INEOS
类别:SBC SBC
用途:薄膜;杯子;医疗器械;片材;玩具;容器;食品包装;盖子;
颜色:清晰/透明
加工条件:吹塑成型
性能特点: 嵌段共聚物; 印刷性好; 透湿性; 透气性高; 透光性好; 韧性好; Good Clarity,Good flexibility,Good Printability,Permeability,Moisture Permeability,Block Copolymer
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.01 | g/cm³ | ASTM D792 |
密度 Density |
1.01 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
11 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
200℃,5 kg 200℃,5 kg |
11.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
0.30 to 1.0 | % | ISO 294-4 |
MD MD |
% | ASTM D955 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
饱和,23℃ Saturation, 23 ℃ |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弹性模量 Elastic modulus |
|||
TD TD |
MPa | ASTM D882 | |
MD MD |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
MD,断裂 MD, fracture |
% | ISO 527-3 | |
MD,断裂 MD, fracture |
% | ASTM D882 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD MD |
g | ASTM D1922 | |
撕裂强度 tear strength |
|||
TD TD |
g | ASTM D1922 | |
氧气传输速率 Oxygen transfer rate |
|||
23℃,0% RH 23℃,0% RH |
cm³/m²/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance 2 |
|||
23℃ 23℃ 2 |
g/m²/24 hr | ASTM F1249 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
ISO 179 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ |
kJ/m² | ISO 180-A | |
23℃ 23℃ |
kJ/m² | ISO 180-A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
Peak force Peak force |
J | ASTM D3763 | |
Total energy Total energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed 3 |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,退火 0.45 MPa, annealed 3 |
℃ | ISO 75-2/B | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
MD MD |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电常数 Dielectric constant |
|||
100 Hz 100 Hz |
IEC 60250 | ||
1.00 mm,1 MHz 1.00 mm,1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index 5 |
ASTM D542 | ||
折射率 Refractive index |
ISO 489 | ||
透光率 Transmittance |
|||
550 nm 550 nm |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0% to 85% RH gradient |
3 4h/80°C |
4 标准 B (120°C/h), 压 力1 (10N) |
5 Sodium D Line |
【新闻资讯】查看全部
顶级手套净利润下跌近五成
2021-10-10 搜料网资讯: 全球最大医用橡胶手套制造商马来西亚顶级手套(Top Glove)近日公布的统计数据显示,今年6至8月,该公司的利润同比下跌了48%。分析称,疫苗接种推进导致医用手套需求下降 |
顶级手套净利润下跌近五成 搜料网资讯:全球最大医用橡胶手套制造商马来西亚顶级手套(Top Glove)近日公布的统计数据显示,今年6至8月,该公司的利润同比下跌了48%。分析称,疫苗接种推进导致医用手套需求下降。 当期净利润为6.079亿林吉特。去年同期净利润为11.7亿林吉特。大幅低于全球金融信息和风险管理提供商路孚特(Refinitiv)的市场预期。销售额为21.1亿林吉特,同比下降32%。 美国以涉嫌强迫劳动而实施的禁运也使顶级手套的业绩受到沉重打击。为期近13个月的禁运于9月10日解除。该公司的一次性手套同时拿到了美国海关部门的产品进口许可。顶级手套表示,尽管禁运解除后对美国的销售将有所增加,但公司的经营环境依然严峻,市场竞争非常激烈。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
第三方认证:
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。