牌号简介 About |
---|
埃奇得 1023JA树脂是一种茂金属乙烯-乙烷共聚物。 由埃奇得 1023JA树脂制成的薄膜具有卓越的抗张强度、冲击强度和抗穿刺性。 这些卓越的强度性能连同良好的拉伸性使该树脂成为一种通用的包装薄膜用树脂。 Exceed 1023JA resin is an ethylene 1-hexene copolymer. Films made from Exceed 1023JA resin have outstanding tensile, impact strength and puncture. These superior strength properties, along with excellent drawability, makes this resin a very versatile packaging film resin. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
|||
1% 正割,TD 1% secant, TD |
239 | MPa | ASTM D882 |
1% 正割,MD 1% secant, MD |
226 | MPa | ASTM D882 |
拉伸强度 tensile strength |
|||
TD,断裂 TD, fracture |
41.2 | MPa | ASTM D882 |
TD,屈服 TD, yield |
10.5 | MPa | ASTM D882 |
MD,断裂 MD, fracture |
MPa | ASTM D882 | |
MD,屈服 MD, yield |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
TD,断裂 TD, fracture |
% | ASTM D882 | |
MD,断裂 MD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD MD |
g | ASTM D1922 | |
撕裂强度 tear strength |
|||
TD TD |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45° 45° |
ASTM D2457 | ||
雾度 Haze |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
第一届尼龙(PA)再生改性技术和市场研讨会将召开
2016-12-09 各会员单位: PA 再生料的应用领域不断扩大,PA 废料、再生料的回收、再生、改性、应用受到大家的关注。为了搭建再生PA 上下游交易平台,解决生产过程中的技术问题,稳定产品质量,提高现有产品的附加值,开发新产品,降低采购成本,拓宽采购渠道,扩大销售领域,中国废塑料协会、中国合成树脂供销协会塑料循环利用分会、“废塑料那些事”新媒体特举办尼龙(PA)再生改性技术和市场研讨会。 一、会议议题 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |