TPX® RT31 TPX® RT31是一种聚甲基戊烯共聚物(PMP 共聚物)材料,。 该产品在欧洲或亚太地区有供货,加工方式为:注射成型。 TPX® RT31的主要特性有: 坚硬 无气味/无味道 TPX® RT31的典型应用领域为:食品接触应用 TPX® RT31 TPX® RT31是一种聚甲基戊烯共聚物(PMP 共聚物)材料,。 该产品在北美洲有供货,加工方式为:管路挤出成型、挤出、纤维(纺纱)挤出、型材挤出成型或注射成型。 TPX® RT31的主要特性有: 高刚度 无气味/无味道 TPX™ RT31 TPX™ is a 4-methylpentene-1-based olefin copolymer. TPX™ has a unique molecular structure. Although TPX™ is a crystalline olefin polymer, it shows transparency. Because of its excellent heat-resistance, release property and chemical resistance, TPX™ is used for industrial materials, including mandrels and sheaths in the manufacture of high-pressure rubber hose, mold cups to create LED light and other applications such as release film on FPC manufacturing process and release paper in the manufacture of synthetic leather. Furthermore, TPX™ possesses a lowest density among thermoplastic polymers and then provides the molded articles with lower weight. This leads to reduce the environmental load for transportation. It is also noted that TPX™ is a halogen-free polymer denoted as environmentally-friendly material. TPX™ is also used for food-related applications such as food wraps, food preservation packs, baking carton and microwave oven tableware TPX™ RT31 TPX™ RT31 is a Polymethylpentene Copolymer (PMP Copolymer) material. It is available in North America for extrusion, fiber (spinning) extrusion, injection molding, pipe extrusion, or profile extrusion. Important attributes of TPX™ RT31 are: High Stiffness Low to No Odor/Taste |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.833 | g/cm³ | 内部方法 |
熔体质量流动速率 Melt Flow Rate |
|||
260℃,5.0kg 260℃,5.0kg |
21 | g/10min | 内部方法 |
螺旋流动长度 Spiral flow length 3 |
51.0 | cm | 内部方法 |
收缩率 Shrinkage rate |
内部方法 | ||
MD:2.0 mm,注塑成型 MD: 2.0 mm, injection molded |
1.6 | % | 内部方法 |
TD:2.0 mm,注塑成型 TD: 2.0 mm, injection molding |
1.3 | % | 内部方法 |
吸水率 Water absorption rate |
|||
平衡 balance |
% | ASTM D570 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,注塑成型 23 ℃, injection molding |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
kJ/m² | ASTM D4812 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 7 |
|||
0.45 MPa,未退火,6.35 mm,注塑 0.45 MPa, unannealed, 6.35 mm, injection molded 7 |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 8 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion 9 |
|||
MD:-10~160℃ MD:-10~160℃ 9 |
1/℃ | 内部方法 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
2 mm 2 mm |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
2 mm,注塑成型 2 mm, injection molding |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
2.00 mm,1 MHz 2.00 mm,1 MHz |
ASTM D150 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index 10 |
ASTM D542 | ||
透光率 Transmittance 11 |
|||
注塑成型 injection molding 11 |
% | ASTM D1003 | |
雾度 Haze 11 |
|||
注塑薄膜 Injection molded film 11 |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级,23℃,注塑成型 R-grade, 23 ℃, injection molding |
ASTM D785 | ||
拉伸模量 Tensile modulus 4 , 5 |
|||
23℃,注塑成型 23 ℃, injection molding 4 , 5 |
MPa | ASTM D638 | |
拉伸强度 tensile strength 4 , 5 |
ASTM D638 | ||
屈服,23℃,注塑成型 Yield, 23 ℃, injection molding |
MPa | ASTM D638 | |
断裂,23℃,注塑成型 Fracture, 23 ℃, injection molding |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 4 , 5 |
|||
断裂,23℃,注塑成型 Fracture, 23 ℃, injection molding 4 , 5 |
% | ASTM D638 | |
弯曲模量 Bending modulus 6 |
|||
23℃,3.20 mm,注塑成型,51 mm跨距 23 ℃, 3.20 mm, injection molding, 51 mm span 6 |
MPa | ASTM D790 | |
弯曲强度 bending strength 6 |
|||
23℃,3.20 mm,注塑成型,51 mm跨度 23 ℃, 3.20 mm, injection molding, 51 mm span 6 |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 模具温度: 163°F, 熔体温度: 590°F |
3 260 to 280°C |
4 类型 4, 2.0 in/min |
5 0.051 in/min |
6 120°C/hr |
7 速率 A (50°C/h), 压 力1 (10N) |
8 Injection Molded |
9 Injection Molded, 2 mm, 589 nm wavelength |
【新闻资讯】查看全部
抚顺石化打造“加速器”:“闭关”修“炼”增强内功
2021-05-10 搜料网资讯: 我们利用装置大检修在烯烃线开展技术改造项目,仅80万吨/年乙烯装置裂解炉更换高效炉管技术改造一项,预计每台裂解炉每年就可降低燃料气消耗1%,延长清焦周期30%。 |
抚顺石化打造“加速器”:“闭关”修“炼”增强内功 搜料网资讯:“我们利用装置大检修在烯烃线开展技术改造项目,仅80万吨/年乙烯装置裂解炉更换高效炉管技术改造一项,预计每台裂解炉每年就可降低燃料气消耗1%,延长清焦周期30%。”5月5日,在抚顺石化检修现场,技术人员介绍说。
抚顺石化是集“油化塑洗蜡剂”为一体的大型石油化工联合企业,烯烃线是主要的创效单位,拥有80万吨/年乙烯等14套生产和辅助装置。近年来,这个公司先后开展尾气回收、树脂包装改造等数十项装置技术攻关,并逐步形成一套装置生产与技术改造同步促进的管理模式,有效促进了生产装置能耗降低和平稳率提高,乙烯产量连年突破设计值,去年产量达到86.52万吨,2020年实现账面利润17.7亿元,创效能力同比增长16.4%,技术创新已经成为这个公司的创效“加速器”。 今年4月份检修以来,这个公司组织烯烃线通过强化管理、优化施工、责任到人等措施,现场解决技术难题,大力推进45项(非常规项目、资本性支出项目、技改技措项目等)技术改造项目的实施。 35万吨/年高密装置流化床由于设计原因,进行串联牌号生产时无法实现长周期运行。去年,技术人员积极攻关,利用状态小修时机进行试验性改造后,流化床生产周期由1个月延长至3个月。今年,他们将充分总结试验性改造的经验,对流化床系统进一步攻关,改造后运行周期将再次大幅提升。 凝液回收是仓储装置大检修中主要技改项目,这个装置在化工液体装卸站生产时,管廊每小时会产生2吨左右的蒸汽凝液,为了将凝液回收外送,技术人员将蒸汽凝液引入新增凝结水橇块的缓冲罐中,有效回收利用。 环保项目也是抚顺石化检修中主要的技改项目。45万吨/年线性低密度聚乙烯装置集尘器排放口高度为10米,随着国家环保要求标准的提高,集尘器排放口高度已经不符合挥发性排放的相关要求。这个公司开展了集尘器排放口技术改造,为了提高改造效率优化施工,依托装置现有管廊支架和基础结构进行技改,仅用3天时间完成施工任务,并安装了符合要求的环保检测采样点。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。