牌号简介 About |
---|
Ultradur® S 4090 G4是一种20%玻璃增强PBT+ASA混合物。它生产的模具具有良好的表面光洁度,耐化学药品和应力开裂,具有低收缩和翘曲。应用领域包括汽车、电气和家用领域的高压力设备外壳。 Ultradur S 4090 G4 is a 20% glass reinforced PBT+ASA blend. It produces moldings with good surface finish, is resistant to chemicals and stress cracking, and has low shrinkage and warpage. Applications Applications include highly stressed equipment housings in the automotive, electrical and household sectors. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.39 | g/cm³ | ASTM D792 |
密度 Density |
1.39 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
275℃,2.16 kg 275℃,2.16 kg |
20.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
MD:3.2 mm MD:3.2 mm |
0.30 | % | |
TD TD |
0.74 | % | ISO 294-4 |
MD MD |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
饱和 saturated |
% | ASTM D570 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
平衡,50% RH Balance, 50% RH |
% | ASTM D570 | |
粘度值 Viscosity value |
|||
降低的粘度 Reduced viscosity |
ml/g | ISO 1628 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
断裂,-40℃ Fracture, -40 ℃ |
MPa | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
断裂,80℃ Fracture, 80 ℃ |
MPa | ISO 527-2 | |
断裂,120℃ Fracture, 120 ℃ |
MPa | ISO 527-2 | |
断裂,150℃ Fracture, 150 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
ISO 527-2 | ||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
断裂,-40℃ Fracture, -40 ℃ |
% | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
断裂,80℃ Fracture, 80 ℃ |
% | ISO 527-2 | |
断裂,120℃ Fracture, 120 ℃ |
% | ISO 527-2 | |
断裂,150℃ Fracture, 150 ℃ |
% | ISO 527-2 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
23℃ 23℃ |
kJ/m² | ISO 180 | |
-40℃ -40℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ||
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
0.71 mm 0.71 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
0.71 mm 0.71 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
0.71 mm 0.71 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity 2 |
ohms | ASTM D257 | |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
1.50 mm 1.50 mm |
ohms·cm | ASTM D257 | |
介电常数 Dielectric constant |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.71 mm 0.71 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 1.5 mm |
【新闻资讯】查看全部
科莱恩推出 FIXAT™ Optimum:最大程度减少霉菌毒素对饲料的影响,让动物
2021-12-15 搜料网资讯: ●霉菌毒素会显著影响动物的增重和饲料转化率 ● FIXAT Optimum 符合法规EC 1060/2013 1m558,可保护饲料免受霉菌毒素污染,包括剧毒的黄曲霉毒素 ● 该解决方案具有成本效益 |
科莱恩推出 FIXAT™ Optimum:最大程度减少霉菌毒素对饲料的影响,让动物 搜料网资讯:●霉菌毒素会显著影响动物的增重和饲料转化率 ●FIXAT Optimum 符合法规EC 1060/2013 1m558,可保护饲料免受霉菌毒素污染,包括剧毒的黄曲霉毒素 ●该解决方案具有成本效益,有助于延长饲料的保质期 科莱恩推出最新解决方案,可对抗由霉菌形成的危险霉菌毒素,这类毒素在全球饲料生产中的发生率高达25%。科莱恩在西班牙nutriFORUM会议上推出的FIXAT Optimum,可保护动物免受这类危险毒素的侵害,包括剧毒的黄曲霉毒素。 霉菌毒素是由在恶劣条件下生长和储存的饲料中产生的霉菌形成的。预计气候变化导致的频繁旱涝和其他自然灾害将使当今形势更加严峻。饲料中霉菌毒素的存在会导致动物的生长参数(如增重和饲料转化率)显著降低,还会造成器官损伤或繁殖问题,导致动物生产收入的巨大损失。更令人担忧的是,霉菌毒素会被带入肉、蛋和乳制品中,从而危害人体。 FIXAT Optimum是一种新开发的吸附剂,由膨润土构成。膨润土是一种珍贵的粘土矿物,具有强大的膨胀性和吸附力。它通过将动物饲料中的霉菌毒素固定在表面,与霉菌毒素分子的极性基团发生静电相互作用,从而去除霉菌毒素。 科莱恩欧洲、中东和非洲地区净化和饲料业务部负责人安祺铎(Guido Appl)表示:“这种新的解决方案可以吸附动物胃肠道中的霉菌毒素。即使在这样恶劣的条件下,该吸附剂也能牢牢吸附毒素,并在不造成损害的情况下将其排出体外。我们在实验室完全复制了吸收和解吸的条件,以测试我们产品的性能。” FIXAT Optimum 适用于全品种、全年龄和各种类的动物,适用于各种饲料,且符合法规EC 1060/2013 1m558。这是一种代谢友好型解决方案,不会留下霉菌毒素代谢物的残留,可有效延长饲料的保质期,确保产量。
从饲料到肉和乳制品的霉菌毒素循环
科莱恩的功能性矿物团队在西班牙nutriFORUM展会上 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
- 汽车车窗开关组件
- 2019-08-14 0
- Ultradur® S 4090 G4是一种20%玻璃增强PBT+ASA混合物。它生产的模具具有良好的表面光洁度,耐化学药品和应力开裂,具有低收缩和翘曲。应用领域包括汽车、电气和家用领域的高压力设备外壳。
- 阅读全文
汽车车窗开关组件
- 发动机中央控制单元壳体
- 2019-04-08 0
- Ultradur® S 4090 G4是一种20%玻璃增强PBT+ASA混合物,具有良好的表面光洁度,耐化学药品和应力开裂
- 阅读全文
发动机中央控制单元壳体
2-熔体体积流动速率(275℃/2.16 kg),20.0 cm³/10 min
3-拉伸模量(23℃),6900MPa
4-简支梁缺口冲击强度(23℃),7.0kJ/m²
- 梅赛德斯ABS外壳
- 2019-04-11 0
- Ultradur® S 4090 G4是一种20%玻璃增强PBT+ASA混合物。材料具有低收缩和翘曲
- 阅读全文
梅赛德斯ABS外壳
2-熔体体积流动速率(275℃/2.16 kg),20 cm³/10min
- 汽车发动机中央控制单元壳体插头
- 2019-04-01 0
- Ultradur® S 4090 G4是一种20%玻璃增强PBT+ASA混合物,材料具有良好的表面光洁度,耐化学药品性好
- 阅读全文
汽车发动机中央控制单元壳体插头
2-MVR( 275℃/2.16 kg),20 cm³/10 min
3-拉伸模量(23℃),6900MPa
4-简支梁缺口冲击强度(23℃),55.0kJ/m²
抱歉!暂无数据。