牌号简介 About |
---|
Telcar® TL-8730R是一种高性能、阻燃热塑性弹性体,设计用于要求在宽温度范围内具有灵活性的电气应用。Telcar® TL-8730R是一个高硬度等级,是紫外线稳定和符合RoHS。该等级为UL认证,适用于注塑和挤压。 Telcar TL-8730R is a high performance, flame retardant thermoplastic elastomer designed for electrical applications requiring flexibility over a wide temperature range. Telcar TL-8730R is a high durometer grade that is UV stablized and RoHS compliant. This grade is UL listed and is suitable for both injection molding and extrusion. |
产品描述 Product Description
厂家:美国特诺尔爱佩斯 Teknor Apex
类别:TPE TPE
用途:电缆护套;电气元件;电气/电子应用领域;电线电缆应用;电线护套;通用;橡胶取代;绝缘材料;
颜色:不透明
加工条件:挤出 Extrusion
性能特点: 防火阻燃等级V-0; 卤化; 硬度高; 防火阻燃等级V-2; 流动性中等; 弯曲性能好; 阻燃; 耐候抗UV; 耐老化; 拉伸性能好; 高密度; 着色性好; 耐臭氧; 韧性好; Weather resistance is good,Good heat aging resistance,Good flexibility,High elastic,Good Hardness,Flame Characteristics,Good Tensile Strength,Moderate liquidity,High density,Ozone resistance,Halogenated,Good coloring,V-2,V-0
紫外线:UV Stabilized
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.24 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
16 | g/10min | ASTM D1238 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 , 3 |
|||
断裂,0.508 mm Fracture, 0.508 mm 2 , 3 |
12.4 | MPa | ASTM D412 |
300% 应变,0.508 mm 300% strain, 0.508 mm 2 , 3 |
6.21 | MPa | ASTM D412 |
100% 应变,0.508 mm 100% strain, 0.508 mm 2 , 3 |
4.48 | MPa | ASTM D412 |
拉伸应变 Tensile strain 2 , 3 |
|||
断裂,0.508 mm Fracture, 0.508 mm 2 , 3 |
% | ASTM D412 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ASTM D2240 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
连续使用温度 Continuous use temperature |
℃ | UL 1581 | |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
|||
136℃,168 hr 136℃,168 hr |
% | ASTM D573 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
|||
136℃,168 hr 136℃,168 hr |
% | ASTM D573 | |
拉伸强度的变化率 The rate of change in tensile strength |
|||
60℃,168 hr,in IRM 902 Oil 60℃,168 hr,in IRM 902 Oil |
% | ASTM D471 | |
Change in Ultimate Elongation(60℃,168 hr,in IRM 902 Oil) Change in Ultimate Elongation(60℃,168 hr,in IRM 902 Oil) |
% | ASTM D471 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1 kHz 1 kHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm,所有颜色 1.50 mm, all colors |
UL 94 | ||
1.50 mm,本色,黑色,白色 1.50 mm, natural color, black, white |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ASTM D2863 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具, 20 in/min |
3 die cut from extruded tapes |
【新闻资讯】查看全部
【干货】影响改性PP塑料收缩率的4大因素
2020-12-30 搜料网资讯: PP塑料的收缩率控制是PP改性的重要方面,收缩率控/制的好对聚丙烯改性料的推广使用有重要意义。特别是应用改性聚丙烯取代传统的工程塑料,收缩率这一点显得十分重 |
【干货】影响改性PP塑料收缩率的4大因素 搜料网资讯:PP塑料的收缩率控制是PP改性的重要方面,收缩率控/制的好对聚丙烯改性料的推广使用有重要意义。特别是应用改性聚丙烯取代传统的工程塑料,收缩率这一点显得十分重要。在改性过程中,对PP塑料收缩率产生影响的有哪些因素呢? 一、矿物填充 PP塑料改性用的矿物添加剂主要有碳酸钙、滑石粉、云母粉等,对PP塑料成型收缩率的影响比较明显。 主要体现在三个方面:一是矿物填加剂本身不收缩,它的加入从整体比例上降低了聚丙烯改性料的收缩率;二是矿物填加剂的加入必然影响聚丙烯的结晶度,从而影响收缩率;三是微细的矿物剂加入后,起到一种成核剂的作用,改变了聚丙烯的结构状态,放大的球晶的形成,也影响聚丙烯的成型收缩率。 二、玻纤增强 玻纤增强是PP塑料改性的一种重要手段,玻纤对PP改性料成型收缩率的影响最大。当玻璃纤维的含量达到30%时以上时,PP塑料的成型收缩率从1.8下降至0.5,而且表面处理过的玻纤对成型收缩率影响大于未进行处理的玻纤。 玻纤的加入破坏了PP的结晶度,影响收缩率,同时玻璃纤维限制了PP塑料的结晶收缩。 三、聚乙烯的加入 聚乙烯也是一种高结晶度的塑料,成型收缩率也很大,但在加入聚丙烯中后相互都不同程度地破坏了各自的结晶度,使整体成型收缩率下降。 四、PP塑料自身MI(熔融指数)的变化 聚丙烯的成型收缩率受其结晶度的影响,而结晶度又受其自身分子量大小的影响。当MI增大时,分子量减小,其结晶速度增大,成型收缩率增大。聚丙烯MI变化时对成型收缩率也有一定的影响。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。