牌号简介 About |
---|
Lexan Exl1414树脂Lexan Exl1414聚碳酸酯(PC)硅氧烷共聚物树脂是一种中等流动性不透明注塑(IM)级树脂。与标准PC相比,该树脂具有极低的温度(-40 C)延展性,同时具有良好的加工性和释放性,有机会缩短IM循环时间。LEXAN™ EXL1414 resin是一种可用于各种不透明颜色的产品,可能是多种应用的最佳选择。 LEXAN EXL1414 polycarbonate (PC) siloxane copolymer resin is a medium flow opaque injection molding (IM) grade. This resin offers extreme low temperature (-40 C) ductility in combination with excellent processability and release with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1414 resin is a product available in wide range of opaque colors and may be an excellent candidate for a wide variety of applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.18 | g/cm³ | ASTM D792 |
密度 Density |
1.19 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
10 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
9.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD:3.2 mm TD:3.2 mm |
0.40 to 0.80 | % | 内部方法 |
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 7 |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 8 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 8 |
ISO 180/1U | ||
-30℃ -30℃ |
ISO 180/1U | ||
23℃ 23℃ |
ISO 180/1U | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 9 |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,100 mm跨距 1.8 MPa, unannealed, 100 mm span 9 |
℃ | ISO 75-2/Ae | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,100 mm跨距 0.45 MPa, unannealed, 100 mm span 9 |
℃ | ISO 75-2/Be | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 10 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~80℃ TD:23~80℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:23~80℃ MD:23~80℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
0.8 mm,在油中 0.8 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
100 Hz 100 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
100 Hz 100 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.40 mm 0.40 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.80 mm 0.80 mm |
℃ | IEC 60695-2-12 | |
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength 3 |
|||
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
屈服 yield |
MPa | ISO 527-2/50 | |
屈服 yield 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture |
% | ISO 527-2/50 | |
断裂 fracture 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
屈服 yield 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
L 级 Level L |
ASTM D785 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*3 sp=62mm |
8 80*10*3 |
9 120*10*4 mm |
10 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
碳酸钙行业明确三大发展路径
2021-08-09 搜料网资讯: 完善产销链条 提升产业层次 更新技术设备 未来5年既是我国无机盐工业固本培元、建立具有国际竞争比较优势的关键期,也是行业转向自主创新、积累新技术优势,以及探 |
碳酸钙行业明确三大发展路径 搜料网资讯:完善产销链条 提升产业层次 更新技术设备 “未来5年既是我国无机盐工业固本培元、建立具有国际竞争比较优势的关键期,也是行业转向自主创新、积累新技术优势,以及探索国际分工合作新模式、与相关行业走向融合发展的关键期,同时还是碳酸钙行业综合治理、转型升级、创新发展的关键时期。行业应从完善完整国内产销链,提升产业结构层次,提高新产品、新技术、新设备的获取能力等三方面入手,实现行业提档升级和高质量发展。”这是近日在江西省吉安市举办的2021年全国碳酸钙行业年会上传出的信息。 中国无机盐工业协会副会长兼秘书长陈国福在年会致辞中说,今年下半年随着国内疫情的好转,无机盐产品的需求会好于上半年,产品价格将回升,企业盈利状况也将得到一定改善。虽然碳酸钙市场需求旺盛带来了产量的增长,但行业依旧面临结构调整压力,中低端产品过剩,而高端产品缺乏。由于产能供过于求的状况短期难以改变,也将对产品价格形成冲击,同时行业还面临着巨大的环保压力。 陈国福强调,未来碳酸钙行业迫切需要通过三条路径实现从传统增长模式向高质量发展模式的转变。 首先要进一步挖掘国内市场潜力,完善国内产销链条。行业要加快构建完善的内需体系,着力打通生产、分配、流通、消费各个环节,围绕产业链部署创新链,不断提升“稳链”“补链”“强链”水平。还要加快培育一批符合市场新需求,具有技术制高点水平,具有成长后劲的技术、项目和产品,形成一批有水平、有规模、有效益、有后劲的新的经济增长点、增长极。 其次,要提升产业结构层次。行业应围绕产业链短板,差异化、精细化发展新材料和专用化学品,布局开发高端前沿新材料、新产品, 加强科技创新和技术攻关,集中力量开展系统攻关,强化关键环节、关键领域和关键产品的保障能力。 再次,要提高新产品、新技术、新设备的获取能力。目前碳酸钙行业内大多数企业生产的都是老产品,其工艺、用途、技术和设备需要不断进步和更新。为此,要有广泛的信息来源和合作渠道,要有外脑、外援、外力,并充分利用现代信息技术,依靠敏锐的观察力和判断力,率先获得自己需要的专有技术。同时要找准主要问题所在,制定新的发展战略,重点探索技术创新、产业结构、绿色化、资源配置国际化和质量效益领先等高质量发展的新路径。 会上,中国无机盐工业协会副秘书长叶丽君宣布了“全国碳酸钙企业30强”名单,相关专家从“十四五”规划和低碳技术等方面对企业未来的发展进行了指导。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
- 对讲机外壳
- 2019-01-25 0
- LEXAN™ EXL1414 resin聚碳酸酯(PC)硅氧烷共聚物树脂是一种中等流动性不透明注塑(IM)级树脂。与标准PC相比,该树脂具有极低的温度(-40 C)延展性,同时具有良好的加工性和释放性,有机会缩短IM循环时间。
- 阅读全文
对讲机外壳
2-收缩率(TD:3.2 mm) 0.40-0.80 %
3-弯曲模量(50 mm跨距) 2250 MPa
4-简支梁无缺口冲击强度( -30℃) 无断裂
5-热变形温度(1.8 MPa,未退火,3.2 mm) 124 ℃