拜内尔2200系列树脂是改性乙烯丙烯酸酯树脂。它们含有一种温度稳定的酯,使它们在高温共挤出中发挥作用。它们以颗粒形式提供,用于传统的挤出和共挤设备,设计用于加工聚乙烯(PE)树脂。拜内尔2200系列树脂适用于各种材料。它们最常用于粘合PE、PP、PET和纸张。 BYNEL® Series 2200 resins are modified ethylene acrylate resins. They contain a temperature stable ester which makes them functional in high temperature coextrusions. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyethylene (PE) resins. BYNEL 2200 series resins adhere to a wide variety of materials. They are most often used to adhere to PE, PP, PET and paper. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.940 | g/cm³ | ASTM D792 |
密度 Density |
0.940 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ASTM D1238 |
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ISO 1133 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
48.0 | ℃ | ASTM D1525 |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
CR929飞机全尺寸复合资料机身壁板工艺件试制成功
2018-03-05 日前, CR929飞机首件全尺寸(15×6米)复合材料机身壁板工艺件试制成功,标志着CR929飞机复合材料机身攻关项目进入新的提升阶段。 先进的碳纤维树脂基复合材料以其比强度高、可设计性、抗疲劳性能好、耐腐蚀性强和高阻尼的性能特点,更好地满足民用飞机对安全性、经济性、舒适性和环保性需求的发展目标。在以B787、A350为代表的双通道飞机上,机身结构复合材料用量均超过50%,减轻了飞机重量,提高了结构耐久性,并以更好的耐腐蚀特性,提高了客舱的压力和湿度,增加了乘客的舒适度。< |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |