牌号简介 About |
---|
Ultradur® S 4090 G4 BK05110是一种20%玻璃增强,色素黑色PBT+ASA混合物。它生产的模具具有良好的表面光洁度,耐化学药品和应力开裂,具有低收缩和翘曲。应用领域包括汽车、电气和家用领域的高压力设备外壳。 Ultradur S 4090 G4 BK05110 is a 20% glass reinforced, pigmented black PBT+ASA blend. It produces moldings with good surface finish, is resistant to chemicals and stress cracking, and has low shrinkage and warpage. Applications Applications include highly stressed equipment housings in the automotive, electrical and household sectors. |
产品描述 Product Description
厂家:德国巴斯夫 BASF
类别:PBT+ASA PBT+ASA
用途:电器外壳;家用货品;汽车领域的应用;外壳;
颜色:黑色
加工条件:注射成型 Injection Molding
性能特点: 耐化学性; 低翘曲性; 收缩性低; 表面光泽度好; 抗应力开裂; Low warping,Good surface appearance,Low contractility,Solvent resistance,High ESCR
填料:玻璃纤维 20
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.39 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
275℃,2.16 kg 275℃,2.16 kg |
20.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
0.74 | % | ISO 294-4 |
MD MD |
0.43 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
0.40 | % | ISO 62 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
断裂,-40℃ Fracture, -40 ℃ |
MPa | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
断裂,80℃ Fracture, 80 ℃ |
MPa | ISO 527-2 | |
断裂,120℃ Fracture, 120 ℃ |
MPa | ISO 527-2 | |
断裂,150℃ Fracture, 150 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
ISO 527-2 | ||
断裂,-40℃ Fracture, -40 ℃ |
% | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
断裂,80℃ Fracture, 80 ℃ |
% | ISO 527-2 | |
断裂,120℃ Fracture, 120 ℃ |
% | ISO 527-2 | |
断裂,150℃ Fracture, 150 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电常数 Dielectric constant |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
雅本化学拟定增收购上海朴颐化学
2015-11-20 停牌中的雅本化学18日早间披露了重组标的:拟通过支付现金与发行股票收购上海朴颐化学科技有限公司100%股权。 截至公告披露日,公司以及有关各方正在积极推动各项工作,中介机构正在抓紧对涉及支付现金与发行股票收购资产事项的相关资产进行尽职调查、审计、评估,公司董事会将在相关工作完成后召开会议,审议本次发行股份购买资产的相关议案。重组事项仍存在不确定性,公司股票继续停牌。 |
雅本化学拟定增收购上海朴颐化学 停牌中的雅本化学18日早间新闻披露了资产重组标底:拟根据支付现金与发行股票回收上海市朴颐有机化学高新科技有限责任公司100%股份。 截止公示披露日,企业及其相关多方已经积极主动促进各项任务,中介服务已经赶紧对涉及到支付现金与发行股票回收资产事宜的相关资产开展财务尽职调查、财务审计、评定,企业股东会将在相关工作中进行后召开工作会议,决议此次发售股权选购资产的相关提案。资产重组事宜仍存有可变性,上市公司再次停牌。 来源于:我国原油和化工网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。