牌号简介 About |
---|
Ultramid® C3U是一种注射成型,通用PA6/66级,具有改进的阻燃性。该产品的最小厚度为0.4 mm,经UL认证为94V0。用途:用于抗冲击电气绝缘部件,如接触座和插头连接条。 Ultramid C3U is an injection molding, general purpose PA6/66 grade with improved flame retardance. The product is UL recognized as 94V0 at 0.4 mm minimum thickness. Applications It is used for impact resistant electrical insulating parts such as contact bases and plug connector strips. |
产品描述 Product Description
厂家:德国巴斯夫 BASF
类别:PA66/6 PA66/6
用途:电气元件;通用;电子绝缘;
加工条件:注射成型 Injection Molding
性能特点: 防火阻燃等级V-0; 阻燃; 冲击性能好; High impact resistance,Flame Characteristics,V-0
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.16 | g/cm³ | ASTM D792 |
密度 Density |
1.16 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
275℃,5 kg 275℃,5 kg |
140 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.80 | % | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
8.5 | % | ISO 62 |
饱和 saturated |
% | ASTM D570 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
平衡,50% RH Balance, 50% RH |
% | ASTM D570 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
23℃ 23℃ |
kJ/m² | ISO 180 | |
-40℃ -40℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
1/℃ | ||
MD MD |
1/℃ | ASTM E831 | |
MD MD |
1/℃ | ||
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
阻燃等级(0.38 mm) Flame retardant grade (0.38 mm) |
℃ | UL 746 | |
0.75 mm 0.75 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
阻燃等级(0.38 mm) Flame retardant grade (0.38 mm) |
℃ | UL 746 | |
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
1.50 mm 1.50 mm |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.38 mm 0.38 mm |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
埃克森美孚思索投资13亿美元 晋级英国炼油厂
2017-10-23 埃克森美孚公司正在考虑花费超过10亿英镑(13.2亿美元)来升级英国Fawley最大的炼油厂。消息人士说,这笔钱将用于2018年炼油厂的催化裂化装置,并在2019年在炼油厂建造两座新工厂。一个来源补充说,至少有一个新工厂可能是一个化学设施。目前的石化业务包括炼油级丙烯,甲基乙基酮,高级烯烃和丁基橡胶。 如果确认,这笔投资将是英国以货币形式进行的最大炼油厂升级。世界上最大的上市石油公司埃克森美孚公司并没有公开表示正在考虑在英国进行这样的投资。 该项目将于今年投 |
埃克森美孚思索投资13亿美元 晋级英国炼油厂 埃克森美孚企业已经考虑到花销超出十亿欧元(13.两亿美金)来升級英国Fawley较大 的炼油厂。内部人士说,该笔钱将用以2018年炼油厂的加氢裂化设备,并在2019年在炼油厂修建二座新工厂。一个来源于填补说,最少有一个新工厂可能是一个有机化学设备。现阶段的石油化工业务流程包含炼油厂级pe,甲基乙基酮,高級环己醇和三元乙丙橡胶。 假如确定,该笔投资将是英国以贷币方式开展的较大 炼油厂升級。世界最大的发售石油公司埃克森美孚企业并沒有公布表明已经考虑到在英国开展那样的投资。 该新项目将于2020年投资3500万美金在Fawley修建一个对映异构乙烷液體生产制造工厂,它是自二十世纪八十年代至今在该地域完工的第一条新生产流水线。炼油厂的一些拟议工作中很有可能已经为将2020年的汽柴油规格型号从3.5%改成0.5%充分准备。 埃克森美孚的新闻发言人回绝置评。 Fawley炼油厂有着270,000 b / d的初加工能力。因为它与全国各地最大的城市和飞机场的联络,该工厂是英国电力能源基础设施建设的关键构成部分。大概85%的炼油厂的生产量根据杜绝纽约,谢菲尔德和布里斯托尔的地下排水管水下混凝土。管路将炼油厂联接到伦敦希思罗机场和盖特威克飞机场。 柴油机占Fawley炼油厂生产量的29%,车用汽油,喷气式飞机然料和石脑油各自占28%,11%和9%。预估2018年的维修将是Fawley炼油厂在2年内初次规模性检修。 来源于:PUWORLD |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
原厂数据及认证:
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- 控制单元外壳
- 2019-04-10 0
- Ultramid® C3U是一种注射成型,通用PA6/66级,优异的强度和耐久性,优良的刚性和耐热性的结合,能够适用于复杂的结构成型,并帮助设计开发者开发新造型产品
- 阅读全文
控制单元外壳
1-Ultramid® C3U是一种注射成型,通用PA6/66级
2-熔体体积流动速率(275℃/5.0 kg),140 cm³/10min
2-熔体体积流动速率(275℃/5.0 kg),140 cm³/10min
3-悬臂梁缺口冲击强度(23℃),43 kJ/m²
4-热变形温度(0.45 MPa,未退火),224℃
收起