牌号简介 About |
---|
Amodel AS- 4145 HS聚邻苯二甲酰胺(PPA)是热水可成型45%玻纤增强树脂。主要性能包括高耐热性,在宽的温度范围内具有高强度和刚度、低吸湿性、优异的耐化学性和优良的电性能。 该树脂是汽车电气和电子产品,包括连接器、插座、开关和传感器的理想选择。同时也是发动机罩下保护关键控制系统,如防抱死制动系统、牵引力控制系统、转向系统、发动机电子控制、传动和底盘控制单元等外壳材料的不错选择。快速结晶率和高流动性可以缩短生产周期,从而提高成型效率,降低成本。 -黑色:AS-4145 HS BK 324 Amodel® AS-4145 HS polyphthalamide (PPA) is a a 45% glass reinforced resin that is hot-water moldable. Key properties include high heat resistance, high strength and stiffness over a broad temperature range, low moisture absorption, excellent chemical resistance and excellent electrical properties. This resin is ideal for automotive electrical and electronic applications, including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units. Its rapid crystallization rate and high flow can result in shorter cycles, thereby enhancing molding productivity and lowering costs. Black: AS-4145 HS BK 324 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.55 | g/cm³ | ISO 1183/A |
收缩率 Shrinkage rate |
|||
TD TD |
1.0 | % | ASTM D955 |
MD MD |
0.50 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.21 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
15200 | MPa | ASTM D638 |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2 | |
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
屈服 yield |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
剪切强度 shear strength |
MPa | ASTM D732 | |
泊松比 Poisson's ratio |
ASTM E132 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
kJ/m² | ISO 179-1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火,3.18 mm 1.8 MPa, annealed, 3.18 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,退火,3.2 mm 0.45 MPa, annealed, 3.2 mm |
℃ | ASTM D648 | |
连续使用温度 Continuous use temperature 2 |
℃ | ASTM D3045 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
熔融温度 Melting temperature |
℃ | ASTM D570 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
ASTM E831 | ||
0 到 90℃ 0 to 90 ℃ |
cm/cm/℃ | ASTM E831 | |
149 到 249℃ 149 to 249 ℃ |
cm/cm/℃ | ASTM E831 | |
MD MD |
ASTM E831 | ||
0 到 90℃ 0 to 90 ℃ |
cm/cm/℃ | ASTM E831 | |
149 到 249℃ 149 to 249 ℃ |
cm/cm/℃ | ASTM E831 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
1.59 mm 1.59 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
mm/min | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 3 |
|||
3.20 mm 3.20 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 1200小时 |
3 这些可燃性等级不代表这些材料或任何其他材料在实际着火灾情况下的危险性。 |
【新闻资讯】查看全部
Multinova塑料工厂启用RFID改善了精确性及效率
2018-12-20 Multinova的泡沫塑料工厂日前启用RFID解决方案来跟踪其产品,该方案是由巴西Caxias do Sul的Akron提供。Multinova位于Farroupilha,正通过使用RFID入口式读取器进行订单拣货及识别,改善了准确性及效率。该公司在Bahia及Santa Catarina的子公司也采用了这项技术。 |
Multinova塑料工厂启用RFID改善了精确性及效率 Multinova的泡沫塑料工厂日前启用RFID解决方案来跟踪其产品,该方案是由巴西Caxias do Sul的Akron提供。Multinova位于Farroupilha,正通过使用RFID入口式读取器进行订单拣货及识别,改善了准确性及效率。该公司在Bahia及Santa Catarina的子公司也采用了这项技术。 在部署RFID技术之前,Multinova的拣货和库存盘点工作使用条形码读取器完成。随着RFID系统的使用,员工再也无需手工读取条形码标签进行盘点。员工也无需寻找每件商品的标签以完成订单拣选工作。现在,他们只需简单的将泡沫塑料卷通过入口式读取器,便可完成盘点及识别工作。 公司还对该RFID部署的效果进行了衡量。结果表明,RFID系统提升了安全性并加速了库存盘点及订单准备过程。该公司称,RFID技术减少了60%的人员劳动时间。下一步,该公司将使用RFID技术进行库存自动盘点,并让客户也受益其中。 目前,生产完成后,每个产品都经过RFID入口式读取器转移到库存区域。然后,在装载及交付时,每件商品会再次通过该读取器。 Multinova的物料控制人员Paula Germana称,试验效果良好。Akron为公司提供了RFID项目所需的信息,并安装了必要的设备和系统。 Germana称,条形码方案给公司的运营带来了很多困难。她说:“卷装物品的每个切片都有一个标签,这种订单准备及产品分离过程非常耗时。使用RFID系统,读取器会自动读取标签信息,给我们的运营增加了敏捷性。” 公司在进料区域以及接收及发货码头安装了RFID读取器。Germana说:“接收及发货码头处都安装了入口式读取器。我们还使用笔记本监控及核查了通过入口式读取器的物品数量。” Germana表示,从条形码切换到RFID技术过程中,公司IT人员做了很多工作。她回忆说:“我们的IT人员不停的优化系统的参数,确保了系统部署完毕便可以开始使用。” 来源:FID世界网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。