牌号简介 About |
---|
Kynar树脂是氟化热塑性均聚物。优异的特性:耐化学性、抗紫外线、高阻隔性、高纯度、良好的机械和热机械性能。主要用途:化工防腐、涂装(涂装、共挤)、近海、电线电缆。Kynar® 1000 HD树脂是用于压缩和转移成型的标准级颗粒,用于挤压厚壁零件:块、棒、板、管。 Kynar® resins are fluorinated thermoplastic homopolymers. Outstanding characteristics: chemical resistance, imperviousness to UV, high barrier properties, high purity, good mechanical and thermo mechanical properties. Main applications: corrosion protection in the chemical industry, coating (painting, co-extrusion), off shore, wire and cable. Kynar® 1000 HD resin is a standard grade of granules for compression and transfer molding, for extrusion of thick walled parts: blocks, rods, plaques, tubes. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.77 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
230℃,5 kg 230℃,5 kg |
1.10 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
2.0 | % | ISO 294-4 |
MD MD |
2.0 | % | ISO 294-4 |
吸水率 Water absorption rate |
ISO 62 | ||
饱和,23℃ Saturation, 23 ℃ |
0.030 | % | ISO 62 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
% | ISO 527-2 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
玻璃化转变温度 Glass transition temperature 3 |
℃ | ISO 11357-2 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
熔融温度 Melting temperature 3 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
特殊值 |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
可燃性等级 Flammability level |
IEC 60695-11-10, -20 | ||
0.8 mm 0.8 mm |
|||
1.6 mm 1.6 mm |
|||
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 |
备注 |
---|
3 10°C/min |
【新闻资讯】查看全部
5月份ABS/PS装置检修情况简析
2021-06-07 搜料网资讯: 二季度是石化企业传统检修季,下面主要梳理一下5月份ABS/PS装置检修及生产情况。据不完全统计,目前国内石化生产企业共计7家有检修计划,共涉及总产能171万吨。 石化 |
||||||||||||||||||||||||||||||||||||||||||||||||
5月份ABS/PS装置检修情况简析 搜料网资讯:二季度是石化企业传统检修季,下面主要梳理一下5月份ABS/PS装置检修及生产情况。据不完全统计,目前国内石化生产企业共计7家有检修计划,共涉及总产能171万吨。
表1:5月国内ABS生产企业装置变动表 5月ABS价格相对高位,使终端家电厂对高价存抵触心理,需求的不足导致部分装置临时停车检修。其中天津大沽ABS装置因蒸汽吹扫管道,5月18日停车检修,于5月24日左右陆续重启。其他石化厂基本维持满负荷运行的情况下,供应量不减。另外,6月初吉化检修在即,时长40天左右;辽通化工计划6月底停车检修,时长40天左右;宁波台化计划6月中下旬对部分装置部件检修,预计开工下降1-2成,影响产能预计3000吨附近。
表2:5月国内PS生产企业装置变动表 如表2所示,本月华东透苯停车检修较为集中,部分货源供应偏紧。华南PS装置停车检修不多。目前,国内已停车的广东星辉、宁波台化透苯装置已开工复产。其中江苏赛宝龙、上海赛科均在下旬转产。另外,因装置设备升级,镇江奇美计划自6月1日起降负生产;辽通化工计划6月末停车检修,时长40天左右。 4月份生产装置集中检修对供应端利好逐渐出尽,5月份月内检修损失量比上个月有所减少,供应量有所增加。目前华南部分区域限电生产,导致中小下游开工不足。家电采购旺季也基本结束,进入消费量淡季的ABS/PS难以拉高需求。石化企业下调出厂价格影响市场心态,软弱的供需关系令价格承压,预计后期市场弱势盘整的可能性较大。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。