牌号简介 About |
---|
在博兹实验室生成的数据。非耐化学性要求的高耐热等级应用。 Data generated in BOZ labs. High heat grade for nonchemical resistance required applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.22 | g/cm³ | ASTM D792 |
熔体体积流动速率 Melt Volume Rate |
|||
265℃,1.2 kg 265℃,1.2 kg |
4.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate 2 |
|||
TD TD 2 |
0.50 to 0.80 | % | 内部方法 |
MD MD 2 |
0.50 to 0.80 | % | 内部方法 |
吸水率 Water absorption rate |
ASTM D570 | ||
24hr 24hr |
0.10 | % | ASTM D570 |
平衡,23℃ Equilibrium, 23 ℃ |
% | ASTM D570 | |
平衡,50% RH Balance, 50% RH |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 3 |
MPa | ASTM D638 | |
拉伸强度 tensile strength 4 |
|||
断裂 fracture 4 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
屈服 yield |
MPa | ISO 527-2/50 | |
屈服 yield 4 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
屈服 yield 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 6 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
弯曲强度 bending strength 6 , 7 |
MPa | ISO 178 | |
弯曲强度 bending strength 5 |
|||
屈服,50 mm跨度 Yield, 50 mm span 5 |
MPa | ASTM D790 | |
泊松比 Poisson's ratio |
ASTM D638 | ||
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | ASTM D1044 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 8 |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 8 |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-40℃ -40℃ |
J/m | ASTM D256 | |
-30℃ -30℃ |
J/m | ASTM D256 | |
-20℃ -20℃ |
J/m | ASTM D256 | |
0℃ 0℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 9 |
ISO 180/1A | ||
-40℃ -40℃ |
kJ/m² | ISO 180-1A | |
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
-20℃ -20℃ |
kJ/m² | ISO 180-1A | |
-10℃ -10℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 9 |
ISO 180/1U | ||
-30℃ -30℃ |
ISO 180/1U | ||
23℃ 23℃ |
ISO 180/1U | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 10 |
|||
1.8 MPa,未退火,100 mm跨距 1.8 MPa, unannealed, 100 mm span 10 |
℃ | ISO 75-2/Ae | |
0.45 MPa,未退火,100 mm跨距 0.45 MPa, unannealed, 100 mm span 10 |
℃ | ISO 75-2/Be | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-30~30℃ TD:-30~30℃ |
1/℃ | ASTM D696 | |
MD:-30~30℃ MD:-30~30℃ |
1/℃ | ASTM D696 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
3.2 mm,在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Tensile Bar |
3 2.0 in/min |
4 类型 1, 2.0 in/min |
5 0.051 in/min |
6 0.079 in/min |
7 Yield |
8 80*10*4 sp=62mm |
9 80*10*4 |
10 120*10*4 mm |
【新闻资讯】查看全部
陶氏与蒙牛再度合作!助力塑料循环经济,实现包装再利用
2021-06-15 搜料网资讯: 6月11日,陶氏公司与蒙牛共同向市场宣布已成功实现消费后回收树脂热收缩膜的商业化。作为中国领先的乳制品企业,蒙牛在乳制品包装工艺中采用了陶氏公司的消费后回 |
陶氏与蒙牛再度合作!助力塑料循环经济,实现包装再利用 搜料网资讯:6月11日,陶氏公司与蒙牛共同向市场宣布已成功实现消费后回收树脂热收缩膜的商业化。作为中国领先的乳制品企业,蒙牛在乳制品包装工艺中采用了陶氏公司的消费后回收(PCR)树脂,这也是亚太区食品饮料行业内的首次创新尝试。这款全新配方的单颗粒树脂,具备100%可回收的特性,将被蒙牛应用于乳制品的二次包装工艺中。这次合作再一次体现了陶氏公司最新的可持续发展指标,即到 2030 年通过自身行动或合作伙伴关系,让100万吨塑料得到回收、重复使用、或再生利用,以消除塑料废弃物。
陶氏公司一直与国内诸多回收行业的合作伙伴进行密切合作,从牛奶瓶、饮用水瓶和果汁瓶中回收废弃塑料以及废弃的柔性薄膜,并将其转为 PCR 树脂。在热收缩膜的中间层加入PCR树脂,可制造出性能与原生树脂近似的薄膜。再通过在二次包装工艺中加入可回收的成分,能够帮助像蒙牛这样的品牌商显著减少价值链中的碳排放,同时也能让原本会被废弃的塑料获得新生,助力包装行业的可持续发展。 陶氏公司包装与特种塑料业务部亚太区商务副总裁李明壮( Bambang Candra)表示:“塑料废弃物的终端市场蕴藏了巨大机遇。作为一个新兴的市场领域,它的出现将有助于提升塑料回收和循环利用的行业意识,推动可回收产品的创新研发,进而减少塑料对自然环境的污染。一直以来,陶氏公司致力于能够实现循环经济的创新解决方案,通过不断创新让可回收产品更加适应于国内市场的复杂需求,并最终将其投入市场实现其商业化价值。而这也与我们的战略目标相契合,即为废旧塑料包装赋予新生、遏制资源浪费、减少环境污染。为此,我们需要与蒙牛等行业领导品牌开展合作,从而实现这一目标。” 蒙牛集团执行总裁李鹏程也表示:“此前,蒙牛旗下高端的鲜奶品牌每日鲜语(Shiny Meadow)已与陶氏公司达成合作,成功铺设了全国首条用再生牛奶塑料瓶制成的 ‘塑料道路’。此次双方再度携手延续了我们在塑料循环经济方面做出贡献的轨迹,进一步推进了我们的可持续发展战略部署——通过使用创新的可持续和可回收材料,助力构建更绿色的行业生态闭环。我们有能力引领乳制品行业向可持续目标不断前行,也有实力为其他绿色转型企业树立行业标杆。相信在陶氏公司的鼎力支持下,我们将朝着这一愿景不断迈进,肩负起环境保护的企业社会责任,推动再生塑料的市场普及,帮助减少温室气体的排放,积极应对塑料废弃物带来的诸多挑战,用实际行动来回应广大消费者对环境问题的关切。” |