牌号简介 About |
---|
Kynar 720是偏氟乙烯的半结晶低分子量造粒聚合物。它是一种多用途的工程塑料,具有优异的物理和化学性能平衡,使其能够在广泛的应用中获得高性能服务。它是一种热塑性氟聚合物,能够在标准加工设备中制造。分子量和分子量分布经过精心调整,以提供适合各种加工要求和最终用途应用的等级。Kynar 720适用于单丝、薄、平和吹塑薄膜等精细挤出操作。它也适用于注射成型应用,在非常薄的截面复杂的设计需要良好的熔体流动特性。Kynar 720还建议用于复合结构的共挤,并用作填充或合金Kynar化合物的基体。这种树脂等级的粉末形式可用作Kynar 721聚偏氟乙烯。 Kynar® resins are fluorinated thermoplastic homopolymers. Outstanding characteristics: chemical resistance, imperviousness to UV, high barrier properties, high purity, good mechanical and thermo-mechanical properties. Main applications: corrosion protection in the chemical industry, coating (painting, co-extrusion), off shore, wire and cable. Kynar® 720 resin is a standard grade of granules for injection molding. This product is ANSI/NSF Standard 61 certified. A powder form is available as Kynar® 721 resin. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
吸水率 Water Absorption Water Absorption |
0.03 | % | ISO 62 |
吸湿性 Moisture Absorption Moisture Absorption |
0.015 | % | ISO 62 |
密度 Density Density |
1780 | kg/m³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate Melt Volume Rate |
|||
230℃,5kg 230℃,5kg |
10 | cm³/10min | ISO 1133 |
成型收缩率 Molding Shrinkage Molding shrinkage |
|||
平行 parallel Parallel |
2.0 | % | ISO 294-4 |
法向 normal Normal |
% | ISO 294-4 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
MPa | ISO 527 | |
拉伸强度 Tensile Strength Tensile Strength |
|||
屈服 yld Yield yld |
MPa | ISO 527-2 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
屈服 yld Yield yld |
% | ISO 527 | |
断裂 brk Broken BRK |
% | ISO 527 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature Melting temperature |
℃ | ISO 11357-3 | |
玻璃化转变温度 Glass Transition Temperature Glass Transition Temperature |
℃ | ISO 11357-2 | |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.80 MPa 1.80 MPa |
℃ | ISO 75-1/-2 | |
0.45 MPa 0.45 MPa |
℃ | ISO 75-1/-2 | |
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
℃ | ISO 306/B | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
平行 parallel Parallel |
E-6/K | ISO 11359-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
|||
1.6 mm 1.6 mm |
calss | IEC 60695-11-10 | |
0.8 mm 0.8 mm |
calss | IEC 60695-11-10 | |
极限氧指数 Oxygen Index Oxygen Index |
% | ISO 4589-2 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相对电容率 Relative Permittivity Relative permittivity |
|||
100Hz 100Hz |
IEC 60250 | ||
1MHz 1MHz |
IEC 60250 | ||
耗散因数 Dissipation Factor Dissipation Factor |
|||
100Hz 100Hz |
E-4 | IEC 60250 | |
1MHz 1MHz |
E-4 | IEC 60250 | |
体积电阻率 Volume Resistivity Volume Resistance |
ohm·m | IEC 60093 | |
表面电阻率 Surface Resistivity Surface Resistivity |
ohm | IEC 60093 | |
耐电强度 Electric strength Electric strength |
kV/mm | IEC 60243-1 | |
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
IEC 60112 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 65% R.H. |
【新闻资讯】查看全部
【干货】如何鉴别白色母粒的质量好坏?
2021-02-02 搜料网资讯: 很多人对白色母粒而言看似很陌生却又如此之熟悉,几乎所有人都用过,具有色泽明亮,鲜艳夺目、着色强度高、分散性好,浓度高,白度好,遮盖力强,耐迁移性和耐热 |
【干货】如何鉴别白色母粒的质量好坏? 搜料网资讯:很多人对白色母粒而言看似很陌生却又如此之熟悉,几乎所有人都用过,具有色泽明亮,鲜艳夺目、着色强度高、分散性好,浓度高,白度好,遮盖力强,耐迁移性和耐热性好等特点, 被广泛应用于注塑、吹塑、拉丝、流延、挤塑、吹膜、发泡、片材、管材、抽粒、中空、EVA、吹瓶、片材、家用电器、玩具、包装材料、电线和电缆、塑料袋、 汽车、建材、体育和休闲用品、包装袋、包装瓶等塑料制品行业。
如何鉴别白色母粒质量的好坏? 不妨先了解一下白色母粒的主要技术指标: 1、耐迁移性(级)[≥4] 2、含水率(%)[≤0.30]8、总色差[≤1.50] 3、熔融温度(oC)[125~200] 4、白色母粒分散性:[无色点、条纹] 5、耐晒性(级)[5-8] 6、白色母粒外观粒状,颗粒均匀、色泽一致 7、耐热性(级)[≥4] 如果白色母粒符合上面几点指标要求,则可以判断该白色母粒质量是好的。 白色母粒使用时的注意事项 一、为了减少配色后纤维色差,对白色母粒要进行稀释,控制混入比例,长丝不少于3%~10%,短纤不少于1%~3%,单色膨体连续长丝用三色设备纺制,白色母粒必须在混合后输入挤压机,同时为增加熔体本身的混合能力,可在挤压机段也增设混合装置。 二、白色母粒混入方式在色丝颜色配方确定后,将白色母粒在纺前均匀分散在丙纶切片中,是保证产品质量的关键,具体的混入方法有两类。其一是重法和体积法,在挤压机中或后部将白色母粒熔融后,用小挤压机注入丙纶熔体中,均匀性很好。 三、选择白色母粒时,要按选用范围选用,丙纶色母粒有细旦级、粗旦级之分,粗旦级的白色母粒色不能用于细旦级配色,配色时应考虑纺制纤维的单丝旦数,选择同类级别的白色母粒。 四、选用的白色母粒最好是同一生产厂家的产品,为降低成本应选用高浓白色母粒。白色母粒的颜料有高、中、低档之分,配色时应根据成纤的品质要求,恰当地选择不同级别的白色母粒。 为避免因颜料光、热稳定性不同而引起成品纤维的品质变异,配色时还应选择符合纤维品质要求的,具有相同光、热稳定级别的白色母粒颜色,粗纤维比细纤维需要的浓度低,其白色母粒应用配比正比于纤旦数的平方根。 |