牌号简介 About |
---|
Lumicene MPE M 3410 EP是以己烯为共聚单体的第二代茂金属基中密度聚乙烯。与传统的LLDPE和第一代茂金属聚乙烯相比,鲁米新MPE M 3410 EP的挤出压力低、气泡稳定性好、表观控制能力强,产量高。这些特征的结合带来了显著的下调潜力。Lumicene MPE M 3410 EP特别适用于需要高光泽和高透明度的薄膜应用,特别是在混合和与LLDPE或LDPE共挤时。Lumicene MPE M 3410 EP适用于消费者、工业、食品或卫生包装领域的许多应用,如整理收缩、邮寄膜、重型袋、袋、层压和卫生膜。 Lumicene® mPE M 3410 EP is a second generation metallocene based Medium Density Polyethylene with hexene as comonomer. Lumicene® mPE M 3410 EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The combination of these features brings a significant downgauging potential. Lumicene® mPE M 3410 EP is especially dedicated to film applications where high gloss and high transparency are required, particularly in blend and in coextrusion with LLDPE or LDPE. Lumicene® mPE M 3410 EP is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as collation shrink, mailing film, heavy-duty sacks, bags, lamination and hygiene film. |
产品描述 Product Description
厂家:法国道达尔 TOTAL
类别:mMDPE mMDPE
用途:重包装袋;薄膜;包装;袋子;收缩性薄膜;食品包装;层压板;吹膜;混合;
加工条件:吹塑薄膜
性能特点: 抗氧化; 透光性好; 己烯共聚单体; 良好的测量控制; 表面光泽度好; Good Clarity,Good surface appearance,Good Gauge Control,Inoxidizability,Hexene copolymers
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.934 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.90 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
40 | µm | |
拉伸强度 tensile strength |
|||
MD,屈服,40 µm,吹塑薄膜 MD, yield, 40 µ m, blow molded film |
17.0 | MPa | |
TD,屈服,40 µm,吹塑薄膜 TD, yield, 40 µ m, blow molded film |
18.0 | MPa | |
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
MPa | ||
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
MPa | ||
拉伸应变 Tensile strain |
|||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ||
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ||
落锤冲击 Drop hammer impact |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
g | ISO 7765-1 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD:40 µm,吹塑薄膜 MD: 40 µ m, blow molded film |
N | ||
TD:40 µm,吹塑薄膜 TD: 40 µ m, blow molded film |
N | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,40.0 µm,吹塑薄膜 45 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
% | ISO 14782 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Blown Film Melt Temperature Blown Film Melt Temperature |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
长岭炼化环氧丙烷装置 反应工艺改造项目中交
2021-12-07 搜料网资讯: 近日,长岭炼化环氧丙烷装置反应工艺改造项目主体设备安装就绪,开始仪电等附属设施联合校验,标志着项目全面进入收尾及生产准备阶段。该项目投运后,环氧丙烷装 |
长岭炼化环氧丙烷装置 反应工艺改造项目中交 搜料网资讯:近日,长岭炼化环氧丙烷装置反应工艺改造项目主体设备安装就绪,开始仪电等附属设施联合校验,标志着项目全面进入收尾及生产准备阶段。该项目投运后,环氧丙烷装置运行效率将提升17%,为企业带来更多效益。 长岭炼化环氧丙烷装置产能为10万吨/年,整体工艺为国内首创。在运行过程中,装置反应器内部催化剂活性开始逐渐减弱,而且每台反应器内催化剂失活速率不一,严重影响装置的整体运行效率。经过专业研讨论证,该公司决定新增第四台反应器。 面对项目施工周期长、作业量大、与生产区域交叉等困难,长岭炼化化工部全面统筹,严格落实各项管理制度,从施工人员入场安全教育培训考核,到施工器具、管材入场等,牢牢把住质量关口,并按照“预防为主、事前管理”的原则,不断细化施工方案,确保项目建设如期完成。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。
电邮一份说明书
PDF文档名:搜料网-TOTAL Polyethylene Lumicene® M 3410 EP (EU - Blown Film)证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)