牌号简介 About |
---|
通过选择特定的单体,可以得到结晶的、永久透明的聚酰胺:三唑胺CX。这些晶体非常小,不会散射可见光,而且这种材料对人眼来说是透明的,这就是所谓的微晶性。由于其结晶度,微晶结构保留了重要的特性,如抗应力开裂-无云化。结晶度是可以忽略不计的,但它对成型件的收缩行为没有不利影响。屈氏体cx经历了类似于非晶材料的各向同性收缩。优良的抗紫外性能、高机械强度、永久透明性、高透光性和优异的耐化学性的结合,为三元色谱仪的生产开辟了广阔的应用领域。典型的应用领域包括汽车工业、机械和工程、医疗技术、体育和娱乐业、眼镜生产、化妆品工业以及水处理和过滤技术。TROGAMID CX7323:中等粘性、永久透明的注塑和挤压用聚酰胺 By selecting specific monomers, one can achieve a crystallizable and permanently transparent polyamide: TROGAMID® CX. The crystallites are so small that they do not scatter visible light, and the material appears transparent to the human eye—a property known as microcrystallinity. Because of its crystallinity, the microcrystalline structure retains important properties such as stress cracking resistance — without clouding. The degree of crystallinity is so negligible, however, that it has no adverse effect on the shrinkage behavior of molded parts. TROGAMID® CX undergoes a similar isotropic shrinkage like amorphous materials. The combination of good UV resistance, high mechanical strength, permanent transparency, high transmission and superior chemical resistance opens a wide range of applications for TROGAMID® CX. Typical areas of application are in the automotive industry, machinery and engineering, medical technology, the sports and recreation industry, the glasses production, the cosmetics industry and in water treatment and filter technology. TROGAMID® CX7323: Medium-viscous, permanently transparent polyamide for injection molding and extrusion |
产品描述 Product Description
厂家:德国赢创 Evonik
类别:PA12 PA12
用途:汽车领域的应用;过滤器;光学应用;化妆品;体育用品;工程应用;
加工条件:挤出 Extrusion
性能特点: 耐磨; 吸水率低; 耐化学性; 耐低温冲击; 抗应力开裂; 耐候抗UV; 易加工; 机械强度好; 尺寸稳定性好; 耐刮擦; 透光性好; 冲击性能好; 收缩性低; Good Rigidity,Weather resistance is good,Excellent Processability,Good Clarity,High impact resistance,Good Dimensional Stability,Low or no water absorption,Low contractility,Good wear resistance,Solvent resistance,low-temperature impact resistance,High scratch resistance,High ESCR
紫外线:UV Stabilized
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.02 | g/cm³ | ISO 1183 |
粘数 Viscosity number |
150 到 170 | cm³/g | ISO 307 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
二氧化碳传输速率 Carbon dioxide transfer rate |
|||
20℃,50 µm 20℃,50 µm |
2540 | cm³/m²/24 hr | |
氮传输速率 Nitrogen transfer rate |
|||
20℃,50 µm 20℃,50 µm |
85.0 | cm³/m²/24 hr | |
氧气传输速率 Oxygen transfer rate |
|||
20℃,50 µm 20℃,50 µm |
740 | cm³/m²/24 hr | |
水气透过率 Water vapor transmittance |
|||
23℃,85% RH,110 µm 23℃,85% RH,110 µm |
g/m²/24 hr | ||
渗透 permeation |
|||
二氧化碳:20℃,50.0 µm Carbon dioxide: 20 ℃, 50.0 µ m |
cm³·cm/cm²/sec/bar | ||
氮气:20℃,50.0 µm Nitrogen: 20 ℃, 50.0 µ m |
cm³·cm/cm²/sec/bar | ||
氧气:20℃,50.0 µm Oxygen: 20 ℃, 50.0 µ m |
cm³·cm/cm²/sec/bar | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ||
0℃,完全断裂 0 ℃, completely fractured |
kJ/m² | ||
23℃,完全断裂 23 ℃, completely fractured |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
|||
0℃ 0℃ |
|||
23℃ 23℃ |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
玻璃化转变温度 Glass transition temperature 4 |
℃ | ISO 11357-2 | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ISO 306/A | |
-- -- |
℃ | ISO 306/B | |
熔融温度 Melting temperature 5 |
|||
DSC DSC 5 |
℃ | DSC | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
1/℃ | ||
TD:23~55℃ TD:23~55℃ |
1/℃ | ||
温度指数 Temperature index 6 |
℃ | IEC 216 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
|||
23℃,100 Hz 23℃,100 Hz |
|||
23℃,1 MHz 23℃,1 MHz |
|||
耗散因数 Dissipation factor |
|||
23℃,100 Hz 23℃,100 Hz |
|||
23℃,1 MHz 23℃,1 MHz |
|||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
CTI CTI 7 |
V | ||
解决方案 A Solution A |
V | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.80 mm 0.80 mm |
|||
1.60 mm 1.60 mm |
|||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
动态特性 Dynamic characteristics 8 |
|||
Under load Under load 8 |
Cycles | DIN EN 13443-1 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
球压硬度 Ball hardness |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ||
80℃ 80℃ |
MPa | ||
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ||
屈服,80℃ Yield, 80 ℃ |
MPa | ||
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ||
屈服,80℃ Yield, 80 ℃ |
% | ||
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ||
80℃ 80℃ |
% | ||
拉伸蠕变模量 Tensile creep modulus |
|||
1 hr 1 hr |
MPa | ||
1000 hr 1000 hr |
MPa | ||
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength 3 |
|||
-- -- |
MPa | ||
3.50% 应变 3.50% strain |
MPa | ||
Outer Fiber Strain(at maximum stress) Outer Fiber Strain(at maximum stress) 3 |
% | ISO 178 | |
抗划伤 Anti scratch |
|||
% turbidity increase % turbidity increase |
DIN 52347 | ||
抗磨损性 abrasion resistance |
mg/100 cycles | DIN 53754 |
备注 |
---|
3、5.0 mm/min |
4、10 K/min |
5、2nd Heating |
6、Criterion: stress at yield |
7、100 drops value |
8、Filter Cup |
【新闻资讯】查看全部
前11月我国实际使用外资突破万亿元
2021-12-26 搜料网资讯: 商务部16日发布数据显示,今年1至11月,全国实际使用外资金额10422亿元,突破万亿元大关。 从行业看,服务业实际使用外资金额8239.4亿元人民币,同比增长17%。高技术产 |
前11月我国实际使用外资突破万亿元 搜料网资讯:商务部16日发布数据显示,今年1至11月,全国实际使用外资金额10422亿元,突破万亿元大关。 从行业看,服务业实际使用外资金额8239.4亿元人民币,同比增长17%。高技术产业实际使用外资同比增长19.3%,其中高技术服务业增长20.8%,高技术制造业增长14.3%。 从来源地看,“一带一路”沿线国家和东盟实际投资同比分别增长24.7%和23.7%(含通过自由港投资数据)。 从区域分布看,我国东部、中部、西部地区实际使用外资同比分别增长15.4%、25.8%和13.4%。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
第三方认证:
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- 眼镜镜框
- 2019-05-20 0
- TROGAMID® CX 7323是注塑成型额聚酰胺PA12,具有优良的抗紫外性能、高机械强度、永久透明性、高透光性和优异的耐化学性的结合,为三元色谱仪的生产开辟了广阔的应用领域。体育和娱乐业、眼镜生产
- 阅读全文
眼镜镜框
1-TROGAMID® CX 7323是注塑成型额聚酰胺PA12,具有优良的抗紫外性能
2-拉伸模量(23℃) 1400 MPa
3-简支梁缺口冲击强度(-30℃,完全断裂) 11 kJ/m²
4-水气透过率(23℃,85% RH,110 µm) 8.3 g/m²/24 hr
5-热变形温度(0.45 MPa,未退火) 122 ℃
6-阻燃等级(0.80 mm) HB
2-拉伸模量(23℃) 1400 MPa
3-简支梁缺口冲击强度(-30℃,完全断裂) 11 kJ/m²
4-水气透过率(23℃,85% RH,110 µm) 8.3 g/m²/24 hr
5-热变形温度(0.45 MPa,未退火) 122 ℃
6-阻燃等级(0.80 mm) HB
收起
抱歉!暂无数据。